Winding wire

SHSold® V180 Glide

  • Enamelled round copper wire, solderable and self lubricating
  • Insulated with polyurethane
  • Class 180

SHSold® V180 Glide is an enamelled copper wire of thermal performance class H and allows quick and direct soldering. The most outstanding characteristics of the wire is the possibilty of efficient and safe contacting of the wire ends by quick and exact soldering at solder bath temperatures from 390 °C upwards without prior mechanical removal of the insulation film. This type of enamelled copper wires fulfills the technical requirements of modern winding techniques and can be well impregnated and cast with compounds in accordance with the manufacturer‘s instructions. The excellent thermal resistance characteristics offer protection when wire-wound coils have to be compound cast and when subject to shorttime overloads. The chemical resistance to aggressive liquid and gaseous mediums is limited, and therefore we recommend that you carry out compatibility tests before using this enamelled copper wire. SHSold® V180 Glide can be easily welded and mechanically connected. Sophisticated process technology and process setting ensure easy mouldability, good elongation plus constant and good insulation characteristics of these wires. The final layer of varnish serves the purpose of providing a superior gliding surface, giving the wire excellent windability features at higher speeds, and enabling a higher filling factor plus reduced soiling of the winding machines. The reduced coefficient of friction helps to avoid damage to the wire during winding and thus maintains the insualtion properties of the wire.


Contactors, magnetic coils, relays, small motors, transformers, inverters


IEC / DIN EN 60317-51
UL approved

Delivery forms

Grade 1: 0.112 - 0.710 mm (> 0.710 mm on request)
Grade 2: on request

Technical data

Typical properties of enamelled round copper wire 0.500 mm, with insulation film grade 1

Overall diameter  Bare wire diameter  Adhesion (no cracks in film after winding)  Scrape resistance  Pencil hardness  Elongation at break  Coefficient of friction 
Unit of measure Set value  Actual value (typ.) 
mm  min. 0.524 - max. 0.544 as set value
mm  0.495-0.505 as set value
  mandrel diameter 0.500 mm 1 x d/10 % pre-elongation
≥ 3.100 ≥ 6.000
  H 2H - 3H
≥ 28 ≥ 37
µ  / ≤ 0.110
Temperature index TI  Cut through temperature (pre-heated block)  Dielectric loss factor (bending point)  Heat shock at 200 °C (no cracks in varnish coat after winding)  Solderability 
Unit of measure Set value  Actual value (typ.) 
°C  180 185
°C  230 ≥ 230
(°C) (tan δ)  / ≥ 140
  mandrel diameter 1.120 mm 1 x d / 10 % pre-elongation
at 390 °C  ≤ 4 ≤ 2.5
Dielectrical strength at RT  High voltage discontiniuties 750V  Electrical conductivity 
Unit of measure Set value  Actual value (typ.) 
kV  ≥ 2.4 (twist) ≥ 3 (cylinder)
  ≤ 10 on 30 m ≤ 7 on 100 m
MS/m  58 - 59 ≥ 58.5
Pencil hardness (storage in standard solvent ½ h / 60 °C)  Pencil hardness (storage in alcohol ½ h / 60 °C)  Resistance to commercial impregnants^(1)  Resistance to commercial refrigerants^(1)  Resistance to commercial dry transformer oils^(1)  Resistance to commercial hydraulic oils^(1) 
Set value  Actual value (typ.) 
min. H 2H - 3H
min. H H
/ yes
/ no
/ not recommended
/ no

(1) Due to the variety of individual applications we cannot make any generally binding commitments regarding the compatibility. We recommend testing compatibility with the materials being used.